Array ( [0] => Array ( [id] => 1901 [topology] => 4<sup>3</sup>T197-CA [link_rcsr] => [in_col] => 3 [transitivity] => [3883] [space_group] => Pnma [pearson] => oP24 [cn] => 4 [Year] => 2023 [cn_sort] => 004- [topology_str] => 4^3T197-CA [caid] => 639 [nn] => 0 [name] => [pressure] => [density] => 3.269 [e_gap] => [energy] => 0.344 [bulk_mod] => 391.6 [shear_mod] => 387.7 [vicker_hard] => 69.2 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 1902 [topology] => 4<sup>3</sup>T197-CA [link_rcsr] => [in_col] => 3 [transitivity] => [3883] [space_group] => Pnma [pearson] => oP24 [cn] => 4 [Year] => 2023 [cn_sort] => 004- [topology_str] => 4^3T197-CA [caid] => 639 [nn] => 1 [name] => 4<sup>3</sup>T197-CA [pressure] => [density] => [e_gap] => [energy] => [bulk_mod] => [shear_mod] => [vicker_hard] => [ref_file] => /References/2023_ActaCrystB_79 [publ_year] => 2023 [ref] => doi: <a href="http://doi.org/10.1107/S205252062300255X" target="_blank">10.1107/S205252062300255X</a> ) )
SACADA Database Code: 639 Topology: 43T197-CA # of independent nodes (IN): 3 Transitivity: [3883] Space Group: Pnma Pearson: oP24 Coordination Number (CN): 4 Year: 2023 Download CIF File Download PDF report |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
43T197-CA (SACADA #639) | 3.269 | 0.344 | 391.6 | 387.7 | 69.2 | SACADA¹ | ||
43T197-CA | doi: 10.1107/S205252062300255X |
10559.9653 | 444.3846 | 2057.1038 | -0.0000 | 0.0000 | 0.0000 |
444.3846 | 11370.2430 | 1019.0430 | 0.0000 | 0.0000 | -0.0000 |
2057.1038 | 1019.0430 | 9252.4367 | -0.0000 | 0.0000 | 0.0000 |
-0.0000 | 0.0000 | -0.0000 | 4287.8688 | -0.0000 | -0.0000 |
0.0000 | 0.0000 | 0.0000 | -0.0000 | 5063.1620 | 0.0000 |
0.0000 | -0.0000 | -0.0000 | -0.0000 | 0.0000 | 4498.3716 |