Array ( [0] => Array ( [id] => 1243 [topology] => 3,4<sup>9</sup>T2 [link_rcsr] => [in_col] => 10 [transitivity] => [(10)(20)(13)2] [space_group] => P-1 [pearson] => aP20 [cn] => 3, 4 (1:9) [Year] => 2013 [cn_sort] => 003-004-001-009- [topology_str] => 3,4<sup>9</sup>T2 [caid] => 318 [nn] => 0 [name] => [pressure] => [density] => 2.855 [e_gap] => [energy] => 1.422 [bulk_mod] => 243.3 [shear_mod] => 216.0 [vicker_hard] => 35.2 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 1244 [topology] => 3,4<sup>9</sup>T2 [link_rcsr] => [in_col] => 10 [transitivity] => [(10)(20)(13)2] [space_group] => P-1 [pearson] => aP20 [cn] => 3, 4 (1:9) [Year] => 2013 [cn_sort] => 003-004-001-009- [topology_str] => 3,4<sup>9</sup>T2 [caid] => 318 [nn] => 1 [name] => phaseII [pressure] => 105 [density] => 2.79 [e_gap] => 4.0 [energy] => [bulk_mod] => 316 [shear_mod] => [vicker_hard] => [ref_file] => /References/2013_Carbon_63_562_592 [publ_year] => 2013 [ref] => ) )
SACADA Database Code: 318 Topology: 3,49T2 # of independent nodes (IN): 10 Transitivity: [(10)(20)(13)2] Space Group: P-1 Pearson: aP20 Coordination Number (CN): 3, 4 (1:9) Year: 2013 Download CIF File Download PDF report |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
3,49T2 (SACADA #318) | 2.855 | 1.422 | 243.3 | 216.0 | 35.2 | SACADA¹ | ||
phaseII | 105 | 2.79 | 4.0 | 316 | doi: 10.1016/j.carbon.2013.06.086 |